Influence of Bioactive, Resin and Glass Ionomer luting cements on the fracture loads of dentin bonded ceramic crowns: Failure loads of Ceramic crowns bonded with Bioactive cement

Vohra, Fahim and Altwaim, Manea and Alshuwaier, Abdulaziz and Al Deeb, Modhi and Alfawaz, Yasser and Alrabiah, Mohammed and Abduljabbar, Tariq (2020) Influence of Bioactive, Resin and Glass Ionomer luting cements on the fracture loads of dentin bonded ceramic crowns: Failure loads of Ceramic crowns bonded with Bioactive cement. Pakistan Journal of Medical Sciences, 36 (3). pp. 416-421. ISSN 1682-024X

[thumbnail of 1946-Article Text-12814-2-10-20200303.pdf] Text
1946-Article Text-12814-2-10-20200303.pdf - Published Version

Download (711kB)

Abstract

Objective: To investigate the failure loads of dentin bonded all-ceramic crowns when luted with Bioactive, resin and glass ionomer cements (GIC) in an in-vitro setting.

Methods: This study was conducted at King Saud University, Saudi Arabia, from Nov.2018 to March 2019. In this study, 60 premolar teeth were prepared for dentin-bonded ceramic crowns. Lithium disilicate ceramic crowns fabricated using CAD-CAM technique were cemented to teeth using Bioactive (ACITVA), Resin (Nexus 3 Gen) and GIC (Ketac Cem- Maxicap). Half of the bonded specimens in each group were thermocycled (50000 cycles), however the remaining half were not aged (n=10). Fracture loads of bonded crowns were assessed by exposing them to static axial occlusal loads (1mm/min) using a round ended metal probe in a Universal testing machine. Means and standard deviations among the study groups were compared with ANOVA and Tukey-Kramer multiple comparisons test.

Results: Highest failure loads were observed in resin group without ageing (thermocycling) (689.13±89.41 N), however, the lowest loads were observed in GIC specimens with ageing (243.16±49.03 N). Among non-aged samples, failure loads for Bioactive (480.30±47.26 N) group were less than Resin (689.13±89.41 N) samples but higher than GIC (307.51±45.29 N) specimens respectively. Among the aged specimens, Bioactive (404.42±60.43 N) showed significantly higher failure loads than GIC (243.16±49.03 N), however lower failure loads than Resin (582.33±95.95 N) samples.

Conclusions: Dentin boned crowns with resin cementation showed higher failure loads than Bioactive and GIC luted crowns. Crowns luted with Bioactive cement showed acceptable failure loads for use as restoration on anterior teeth.

Item Type: Article
Subjects: East India Archive > Medical Science
Depositing User: Unnamed user with email support@eastindiaarchive.com
Date Deposited: 20 Apr 2023 07:54
Last Modified: 04 Sep 2024 04:27
URI: http://ebooks.keeplibrary.com/id/eprint/912

Actions (login required)

View Item
View Item